Stainless Steels Hânlieding E2594-15 GXHY methanol dehydrataasje toer elektrodes
WELDING TECHNOLOGY
Lit de fragen net litte
Trochgean mei jo efterfolgje
Arc ynstabiliteit
Unsightly foarmjen
Overmatige spatten
Geskikt foar welding fan duplex RVS
mei 25% Cr, lykas 0022 crni7mo4n03cr25ni6mo3cu2n, ensfh.
Lege wetterstof dûbele faze RVS hân elektrodes, de wichtichste komponint is 25.5Cr-10Ni-4Mo-0.25N
Ripple prima
It lasmetaal is austenityske en ferrityske bifase
struktuer, en de corrosie ferset yndeks is PRE> 40
It hat hege sterkte en goede wjerstân tsjin pitting en stress corrosie cracking.
Prachtige welding technology, stabile bôge, prachtige foarmjen, delikate rimpeling, lytse plons, maklike ferwidering fan slakken.
Maklik slagjen
Produkt parameter
GEMISCHE KOMPONET:
| ALLOY (wt%) | C | Mn | Si | P | S | Ni | Cr | Mo | Cu | Oar |
| GB / T REGELS | 0.033 | 1.05 | 0.76 | 0.019 | 0.011 | 9.1 | 25.5 | 3.9 | 0.11 | N:0.24 |
MEGANISCHE EIENDOM:
| BESIT | YIELD STRENGT (MPa) | EXTENSION STRENGTH (MPa) | IMAPACT WAARDE J/℃ | Waarmtebehandeling °C*h | ||||
| GB / T REGELS | 918 | 22 | - | - | ||||
Oanrikkemandearre weldingparameters:
| DIAMETER SPESIFIKASJES (mm) | 2.0*250 | 2,6*300 | 3,2*350 | 4,0*350 | 5.0*350 | |||||
| ELEKTRISITEIT (Amp) | H/W | 30-55 | 50-85 | 80-120 | 100-150 | 140-180 | ||||
| O/W | 20-50 | 45-80 | 70-110 | 90-135 | - | |||||
Factory stipe
It produkt is geskikt foar in
breed oanbod fan applikaasjes
WELDING TECHNOLOGY
-
Welding materialen foar spoar auto's
Harbin elektryske trije poarte CMT
-
CJ50 jack-up drill
GEMISCHE KOMPONET:
| ALLOY (wt%) | C | Mn | Si | P | S | Ni | Cr | Mo | Cu | Oar |
| GB / T REGELS | 0.033 | 1.05 | 0.76 | 0.019 | 0.011 | 9.1 | 25.5 | 3.9 | 0.11 | N:0.24 |
MEGANISCHE EIENDOM:
| BESIT | YIELD STRENGT (MPa) | EXTENSION STRENGTH (MPa) | IMAPACT WAARDE J/℃ | Waarmtebehandeling °C*h | ||||
| GB / T REGELS | 918 | 22 | - | - | ||||
Oanrikkemandearre weldingparameters:
| DIAMETER SPESIFIKASJES (mm) | 2.0*250 | 2,6*300 | 3,2*350 | 4,0*350 | 5.0*350 | |||||
| ELEKTRISITEIT (Amp) | H/W | 30-55 | 50-85 | 80-120 | 100-150 | 140-180 | ||||
| O/W | 20-50 | 45-80 | 70-110 | 90-135 | - | |||||