Stainless Steels Flux Cored Wire R309LT1-5 LNG auto's flessen welding materiaal
WELDING TECHNOLOGY
Lit de fragen net litte
Trochgean mei jo efterfolgje
Arc ynstabiliteit
Unsightly foarmjen
Overmatige spatten
Geskikt foar RVS en koalstof stiel of lege alloy stiel ûngelikense stiel welding, welding koalstof stielen piip en austenitic roestfrij stiel piip joint boaiem welding.
De wichtichste komponint is lege koalstof 22% Cr-12% Ni
Ripple prima
De rêch sûnder foljen up, kinne jo krije poerbêst weld paad
De foarm fan de weld pass is moai, de slag ferwidering is maklik, en it welding proses hat poerbêste prestaasjes
Maklik slagjen
Produkt parameter
GEMISCHE KOMPONET:
| ALLOY (wt%) | C | Mn | Si | P | S | Ni | Cr | Mo | Oar |
| GB / T REGELS | 0.015 | 0.45 | 1.30 | 0.015 | 0.001 | 12.9 | 24.4 | 0.02 | - |
MEGANISCHE EIENDOM:
| BESIT | YIELD STRENGT (MPa) | EXTENSION STRENGTH (MPa) | Ferlinging/% | IMAPACT WAARDE J/℃ | Waarmtebehandeling °C*h | |||||
| GB / T REGELS | - | 650 | 36 | - | - | |||||
Oanrikkemandearre weldingparameters:
| DIAMETER SPESIFIKASJES (mm) | Dikte fan plating (mm) | Root iepening (mm) | Elektrisiteit (Amp) | |||||
| 2,2*915 | 2~4 | 2.0 | 80-100 | |||||
| 5~9 | 2.5 | 90-120 | ||||||
| ≥10 | 3.0 | 90-130 | ||||||
Factory stipe
It produkt is geskikt foar in
breed oanbod fan applikaasjes
WELDING TECHNOLOGY
-
Welding materialen foar aluminium alloys
-
Trije doarren 2 # is ynaktyf
-
300.000 ton bulkferfier
GEMISCHE KOMPONET:
| ALLOY (wt%) | C | Mn | Si | P | S | Ni | Cr | Mo | Oar |
| GB / T REGELS | 0.015 | 0.45 | 1.30 | 0.015 | 0.001 | 12.9 | 24.4 | 0.02 | - |
MEGANISCHE EIENDOM:
| BESIT | YIELD STRENGT (MPa) | EXTENSION STRENGTH (MPa) | Ferlinging/% | IMAPACT WAARDE J/℃ | Waarmtebehandeling °C*h | |||||
| GB / T REGELS | - | 650 | 36 | - | - | |||||
Oanrikkemandearre weldingparameters:
| DIAMETER SPESIFIKASJES (mm) | Dikte fan plating (mm) | Root iepening (mm) | Elektrisiteit (Amp) | |||||
| 2,2*915 | 2~4 | 2.0 | 80-100 | |||||
| 5~9 | 2.5 | 90-120 | ||||||
| ≥10 | 3.0 | 90-130 | ||||||