Stainless Steels Flux Cored Wire EGT1-4 Reactor komponinten weld
WELDING TECHNOLOGY
Lit de fragen net litte
Trochgean mei jo efterfolgje
Arc ynstabiliteit
Unsightly foarmjen
Overmatige spatten
Geskikt foar welding SUS316Nb en 316Ti
De tafoeging fan Nb kin effektyf ferbetterje de wjerstân tsjin intergranular corrosie
Ripple prima
De bôge is sêft en stabyl, minder spat, prachtige foarming
Goede slagferwidering, stabile wire feeding, mei poerbêste welding proses prestaasjes.
Maklik slagjen
Produkt parameter
GEMISCHE KOMPONET:
| ALLOY (wt%) | C | Mn | Si | P | S | Ni | Cr | Mo | Oar |
| GB / T REGELS | 0.02 | 0.6 | 1,50 | 0.02 | 0.003 | 12 | 19.5 | 2.5 | Nb: 0,25 |
MEGANISCHE EIENDOM:
| BESIT | YIELD STRENGT (MPa) | EXTENSION STRENGTH (MPa) | Ferlinging/% | IMAPACT WAARDE J/℃ | Waarmtebehandeling °C*h | |||||
| GB / T REGELS | - | 650 | 35 | - | - | |||||
Oanrikkemandearre weldingparameters:
| DIAMETER SPESIFIKASJES (mm) | 1.2 | 1.6 | |||
| Spanning (volt) | 22-36 | 26-38 | |||
| Elektrisiteit (Amp) | 120-260 | 200-300 | |||
| Faasje (mm/min) | 15-20 | 18-25 | |||
| Dry stretch lingte (mm) | 15-25 | 15-25 |
Factory stipe
It produkt is geskikt foar in
breed oanbod fan applikaasjes
WELDING TECHNOLOGY
Reaktor ynterne
-
981 semi-submersible drilling rig
-
8,2 ton bulkskip
GEMISCHE KOMPONET:
| ALLOY (wt%) | C | Mn | Si | P | S | Ni | Cr | Mo | Oar |
| GB / T REGELS | 0.02 | 0.6 | 1,50 | 0.02 | 0.003 | 12 | 19.5 | 2.5 | Nb: 0,25 |
MEGANISCHE EIENDOM:
| BESIT | YIELD STRENGT (MPa) | EXTENSION STRENGTH (MPa) | Ferlinging/% | IMAPACT WAARDE J/℃ | Waarmtebehandeling °C*h | |||||
| GB / T REGELS | - | 650 | 35 | - | - | |||||
Oanrikkemandearre weldingparameters:
| DIAMETER SPESIFIKASJES (mm) | 1.2 | 1.6 | |||
| Spanning (volt) | 22-36 | 26-38 | |||
| Elektrisiteit (Amp) | 120-260 | 200-300 | |||
| Faasje (mm/min) | 15-20 | 18-25 | |||
| Dry stretch lingte (mm) | 15-25 | 15-25 |