GEMISCHE KOMPONET:
ALLOY (wt%) | C | Mn | Si | Cr | Ni | Fe | Nb | Mo | P | S |
GB / T REGELS | - | - | - | - | - | - | - | - | - | - |
AWS REGELS | 0.10 | 0,50 | 0,50 | 20.0-23.0 | ≥58,0 | 5.00 | 3.15-4.15 | 8,0-10,0 | 0.02 | 0.02 |
EXEMPEL WAARDE | 0.015 | 0.25 | 0.3 | 22 | 64,00 | 0.3 | 3.3 | 9.5 | 0.0005 | 0.0005 |
MEGANISCHE EIENDOM:
BESIT | YIELD STRENGT (MPa) | EXTENSION STRENGTH (MPa) | IMAPACT WAARDE J/℃ | ELONGATION(%) | ||||
GB / T REGELS | - | - | - | - | ||||
AWS REGELS | - | 690 | - | 25 | ||||
EXEMPEL WAARDE | - | 760 | 80/-196 | 32 |
Oanrikkemandearre weldingparameters:
DIAMETER SPESIFIKASJES (mm) | 1.2 | ||||
Volt | 25-34 | ||||
Amp | 150-250 | ||||
Dry extension lingte (mm) | 15-25 | ||||
Gasstream (l/min) | 20-25 |
De nominale gearstalling wie 60%Ni-22%Cr-9%Mo-3%Fe-3,6%Nb.
-196 ° C lege temperatuer ynfloed prestaasjes is poerbêst.
De bôge is sêft en stabyl, minder splash, moaie foarming, goede slagferwidering, stabile wire feeding, mei poerbêste welding proses prestaasjes.
-
Termyske macht applikaasje
-
Qinghai Youjian Wunan Oilfield
-
20000TEU kontenerskip
GEMISCHE KOMPONET:
ALLOY (wt%) | C | Mn | Si | Cr | Ni | Fe | Nb | Mo | P | S |
GB / T REGELS | - | - | - | - | - | - | - | - | - | - |
AWS REGELS | 0.10 | 0,50 | 0,50 | 20.0-23.0 | ≥58,0 | 5.00 | 3.15-4.15 | 8,0-10,0 | 0.02 | 0.02 |
EXEMPEL WAARDE | 0.015 | 0.25 | 0.3 | 22 | 64,00 | 0.3 | 3.3 | 9.5 | 0.0005 | 0.0005 |
MEGANISCHE EIENDOM:
BESIT | YIELD STRENGT (MPa) | EXTENSION STRENGTH (MPa) | IMAPACT WAARDE J/℃ | ELONGATION(%) | ||||
GB / T REGELS | - | - | - | - | ||||
AWS REGELS | - | 690 | - | 25 | ||||
EXEMPEL WAARDE | - | 760 | 80/-196 | 32 |
RECOMMENDED WELDING PARAMETERS:
DIAMETER SPESIFIKASJES (mm) | 1.2 | ||||
Volt | 25-34 | ||||
Amp | 150-250 | ||||
Dry extension lingte (mm) | 15-25 | ||||
Gasstream (l/min) | 20-25 |