GEMISCHE KOMPONET:
ALLOY (wt%) | C | Mn | Si | Ni | Cr | Mo | P | S |
GB / T REGELS | 0.12 | 1.25 | 0,80 | 3.00-3.75 | - | - | 0.03 | 0.03 |
AWS REGELS | 0.12 | 1.25 | 0,80 | 3.00-3.75 | - | - | 0.03 | 0.03 |
EXEMPEL WAARDE | 0.045 | 0,75 | 0.22 | 3.52 | 0.04 | 0.06 | 0.007 | 0.004 |
MEGANISCHE EIENDOM:
BESIT | YIELD STRENGT (MPa) | EXTENSION STRENGTH (MPa) | IMAPACT WAARDE J/℃ | ELONGATION(%) | Warmtebehanneling °Cxh | |||||
GB / T REGELS | 460 | 550 | 27/-75 | 17 | 605*1 | |||||
AWS REGELS | 460 | 550 | 27/-75 | 19 | 605*1 | |||||
EXEMPEL WAARDE | 495 | 600 | 100/-75 | 26 | 605*1 |
Oanrikkemandearre weldingparameters:
DIAMETER SPESIFIKASJES (mm) | 2,6*350 | 3,2*350 | 4.0*400 | 5.0*400 | ||||
ELEKTRISITEIT (Amp) | H/W | 80-110 | 100-130 | 130-180 | 170-210 | |||
O/W | 60-100 | 80-120 | 120-160 | - |
Izer poeder leech wetterstof type hân elektrodes.
Troch de tafoeging fan izeren poeder is de melting-effisjinsje heger, de impacttaaiheid fan it smelte metaal by -75 ℃.
Stabile bôge, minder spat, goede foarming, maklike slagferwidering, X-Ray-prestaasjes binne poerbêst.
GEMISCHE KOMPONET:
ALLOY (wt%) | C | Mn | Si | Ni | Cr | Mo | P | S |
GB / T REGELS | 0.12 | 1.25 | 0,80 | 3.00-3.75 | - | - | 0.03 | 0.03 |
AWS REGELS | 0.12 | 1.25 | 0,80 | 3.00-3.75 | - | - | 0.03 | 0.03 |
EXEMPEL WAARDE | 0.045 | 0,75 | 0.22 | 3.52 | 0.04 | 0.06 | 0.007 | 0.004 |
MEGANISCHE EIENDOM:
BESIT | YIELD STRENGT (MPa) | EXTENSION STRENGTH (MPa) | IMAPACT WAARDE J/℃ | ELONGATION(%) | Warmtebehanneling °Cxh | |||||
GB / T REGELS | 460 | 550 | 27/-75 | 17 | 605*1 | |||||
AWS REGELS | 460 | 550 | 27/-75 | 19 | 605*1 | |||||
EXEMPEL WAARDE | 495 | 600 | 100/-75 | 26 | 605*1 |
Oanrikkemandearre weldingparameters:
DIAMETER SPESIFIKASJES (mm) | 2,6*350 | 3,2*350 | 4.0*400 | 5.0*400 | ||||
ELEKTRISITEIT (Amp) | H/W | 80-110 | 100-130 | 130-180 | 170-210 | |||
O/W | 60-100 | 80-120 | 120-160 | - |