Low-alloy stielen Hânlieding elektrodes E8018-B3L Seal stuff

GB/T5118 E5518-2C1ML

AWS A5.5E8018-B3L

AWS A5.5M E5518-B3L

ISO 3580-A:E(CrMo2L) B 3 2

ISO 3580-B:E5518-2C1ML

Whatapp: +8613252436578

E-mail: sale@welding-honest.com

Merk:JINGLEI

Model:GER-408L

Netzteil polariteit:DC+/AC

Oarsprong:Sina

Suit foar:Legelegearre stielen

Welding posysje:H/VU/F/OH

Grutte:2.6*350mm 3.2*350mm 4.0*400mm 5.0*400mm

MOQ: 1T Kapasiteit:1200T Per moanne

Betelling:TT, LC

OEM:Kin klantized

Produkt Detail

Leech wetterstof potassium type hân elektrodes hat poerbêste krûp ferset ûnder 550C hege temperatuer arbeidsbetingsten

Stabile bôge, minder spat, goede foarmjen, maklike slakkenferwidering

X-Ray prestaasjes is poerbêst.

GEMISCHE KOMPONET:

ALLOY (wt%)	C	Si	Mn	P	S	Ni	Cr	Mo	Oar
GB / T REGELS	0.046	0,35	0.7	0.015	0.01	0.022	2.18	0.97	-

MEGANISCHE EIENDOM:

BESIT	YIELD STRENGT (MPa)		EXTENSION STRENGTH (MPa)		Ferlinging (%)		IMAPACT WAARDE J/℃		Waarmtebehandeling °C*h
GB / T REGELS	510		605		19		105 / Normaal temperatuer		690*1

Oanrikkemandearre weldingparameters:

300.000 ton offshore Floating Production Storage Tanker (FPSO)

GEMISCHE KOMPONET:

ALLOY (wt%)	C	Si	Mn	P	S	Ni	Cr	Mo	Oar
GB / T REGELS	0.046	0,35	0.7	0.015	0.01	0.022	2.18	0.97	-

MEGANISCHE EIENDOM:

BESIT	YIELD STRENGT (MPa)		EXTENSION STRENGTH (MPa)		Ferlinging (%)		IMAPACT WAARDE J/℃		Waarmtebehandeling °C*h
GB / T REGELS	510		605		19		105 / Normaal temperatuer		690*1