Low-alloy stielen Hânlieding elektrodes E8018-B1 metalen Jointing accessoires

GB/T5118 E5518-CM

AWS A5.5E8018-B1

AWS A5.5M E5518-B1

ISO 3580-A:E(CrMo0.5) B 3 2

ISO 3580-B:E5518-CM

Whatapp: +8613252436578

E-mail: sale@welding-honest.com

Merk:JINGLEI

Model:GER-208

Netzteil polariteit:DC+/AC

Oarsprong:Sina

Suit foar:Legelegearre stielen

Welding posysje:H/VU/F/OH

Grutte:2.6*350mm 3.2*350mm 4.0*400mm 5.0*400mm

MOQ: 1T Kapasiteit:1200T Per moanne

Betelling:TT, LC

OEM:Kin klantized

Produkt Detail

Izer poeder leech wetterstof kalium type hân elektrodes

Stabiele bôge, minder spat, goed foarmjen, maklike slakkenferwidering.

X-Ray prestaasjes is poerbêst.

GEMISCHE KOMPONET:

ALLOY (wt%)	C	Si	Mn	P	S	Ni	Cr	Mo	Oar
GB / T REGELS	0.075	0.33	0.78	0.013	0.009	0.015	0,55	0.53	-

MEGANISCHE EIENDOM:

BESIT	YIELD STRENGT (MPa)		EXTENSION STRENGTH (MPa)		Ferlinging (%)		IMAPACT WAARDE J/℃		Waarmtebehandeling °C*h
GB / T REGELS	520		620		25		130 / Normaal temperatuer		620*1

Oanrikkemandearre weldingparameters:

SG superior nucleus

Wind power applikaasje

GEMISCHE KOMPONET:

ALLOY (wt%)	C	Si	Mn	P	S	Ni	Cr	Mo	Oar
GB / T REGELS	0.075	0.33	0.78	0.013	0.009	0.015	0,55	0.53	-

MEGANISCHE EIENDOM:

BESIT	YIELD STRENGT (MPa)		EXTENSION STRENGTH (MPa)		Ferlinging (%)		IMAPACT WAARDE J/℃		Waarmtebehandeling °C*h
GB / T REGELS	520		620		25		130 / Normaal temperatuer		620*1