Low-Alloy Steels Manual Electrode E7016-C2L Reactor komponinten weld
De wichtichste gearstalling is 3,5% Ni stiel, lege wetterstof kalium type hân welding rod, by -75C wurktemperatuer, syn melting
De trefsterkte fan it metaal is poerbêst.
Stabile bôge, minder splash, goede moulding, maklike slagferwidering, X-Rav-prestaasjes is poerbêst.
GEMISCHE KOMPONET:
ALLOY (wt%) | C | Si | Mn | P | S | Ni | Cr | Mo | Oar | |
GB / T REGELS | 0.038 | 0.19 | 0.64 | 0.006 | 0.004 | 3.56 | 0.033 | 0.8 | - |
MEGANISCHE EIENDOM:
BESIT | YIELD STRENGT (MPa) | EXTENSION STRENGTH (MPa) | Ferlinging (%) | IMAPACT WAARDE J/℃ | Waarmtebehandeling °C*h | |||||
GB / T REGELS | 475 | 550 | 28 | 65/-100 | 620*1 |
Oanrikkemandearre weldingparameters:
DIAMETER SPESIFIKASJES (mm) | 2,6*350 | 3,2*350 | 4.0*400 | 5.0*400 | |||||
ELEKTRISITEIT (Amp) | H/W | 70-100 | 100-140 | 140-180 | 180-230 | ||||
O/W | 60-90 | 90-130 | 120-160 | - |
Reaktor ynterne
-
Qinghai Youjian Wunan oaljefjild
-
308.000 ton VLCC rûge oalje skip
GEMISCHE KOMPONET:
ALLOY (wt%) | C | Si | Mn | P | S | Ni | Cr | Mo | Oar | |
GB / T REGELS | 0.038 | 0.19 | 0.64 | 0.006 | 0.004 | 3.56 | 0.033 | 0.8 | - |
MEGANISCHE EIENDOM:
BESIT | YIELD STRENGT (MPa) | EXTENSION STRENGTH (MPa) | Ferlinging (%) | IMAPACT WAARDE J/℃ | Waarmtebehandeling °C*h | |||||
GB / T REGELS | 475 | 550 | 28 | 65/-100 | 620*1 |
Oanrikkemandearre weldingparameters:
DIAMETER SPESIFIKASJES (mm) | 2,6*350 | 3,2*350 | 4.0*400 | 5.0*400 | |||||
ELEKTRISITEIT (Amp) | H/W | 70-100 | 100-140 | 140-180 | 180-230 | ||||
O/W | 60-90 | 90-130 | 120-160 | - |